Product Details:
|
Raw Material: | Calcined Bauxite | Smelting Furnace: | Tilting Furnace |
---|---|---|---|
Process: | Barmac | Shape: | Micropowder |
Usage: | Polishing | Color: | Grey |
High Light: | Polishing Fused Alumina Powder,Sandblasting Aluminum Oxide,Sandblasting Aluminium Oxide |
Tilting Furnace Barmac Crushing Brown Fused Alumina Micro Powder for Polishing Sandblasting
1. Brown Fused Alumina Descriptions
Brown Fused Alumina is made of high-quality bauxite, anthracite, and iron filings. Because of its low iron content, alumina is often used in blasting operations where iron contamination on the non-ferrous metal substrate is not allowed. Aluminium oxide is a very hard and sharp abrasive that cleans rapidly. It leaves an anchor profile prior to coating and is suitable for removal of scale, rust and old coatings. Furthermore it is used for ceramic grinding wheels, refractory applications and polishing and grinding.
2. Brown Fused Alumina Characteristics
a. High hardness
b. High crystallinity
c. Good linear flow performance
d. Weak adherence
e. No explosion while using
f. No cracking
g. No pulverizing, abrasive product with dark blue color after burning
h. No net cracks and rust
3. Brown Fused Alumina Applications
Brown fused alumina is widely used as a raw material in many industries:
1. Aggregate/Filler.
2. Bonded grinding wheels.
3. Coated Abrasives.
4. Dry blast abrasive.
5. Fine blast media.
6. Loose abrasive.
7. Refractories products.
8. Wet blast abrasive.
4. Brown Fused Alumina Packing
Brown Fused Alumina BFA Packing:
1). 25 kg/bag, in bulk;
2). 25 kg/bag, 40 bags/big bag;
3). 25 kg/ bag, 40 bags/pallet;
4).According to customer's requirement
5. Brown Fused Alumina Specifications
Tilting Furnace (Turn-over Furnace) Barmac Crushing
Items | Unit | Index | Typical | |
Chemical Composition | Al2O3 | % | 95%min | 95.56 |
SiO2 | % | 1.2max | 0.96 | |
Fe2O3 | % | 0.30max | 0.09 | |
TiO2 | % | 3.00max | 2.55 | |
Melting point | ℃ | 2050 | ||
Refractoriness | ℃ | 1980 | ||
True density | g/cm3 | 3.90min | ||
Mohs hardness | --- | 9.00min | ||
Refractory grain sizes | mm | 0-50, 0-1, 1-3, 3-5, 5-8 | ||
Fine powder | mesh | -80, 100, 150, 200, 325F | ||
Abrasives Grits | FEPA | 8, 14, 16, 20, 22,24, 30, 36, 40, 46, 60, 70, 80, 90, 100, 120, 150, 180, 220, 240 | ||
Fixed Furnace Barmac Crushing |
||||
Items | Unit | Index | Typical | |
Chemical Composition | Al2O3 | % | 95%min | 95.23 |
SiO2 | % | 1.5max | 1.28 | |
Fe2O3 | % | 0.30max | 0.17 | |
TiO2 | % | 3.00max | 2.62 | |
Melting point | ℃ | 2050 | ||
Refractoriness | ℃ | 1980 | ||
True density | g/cm3 | 3.90min | ||
Mohs hardness | --- | 9.00min | ||
Refractory grain sizes | mm | 0-50, 0-1, 1-3, 3-5, 5-8 | ||
Fine powder | mesh | -80, 100, 150, 200, 325F | ||
Abrasives Grits | FEPA | 8, 14, 16, 20, 22,24, 30, 36, 40, 46, 60, 70, 80, 90, 100, 120, 150, 180, 220, 240 |