Product Details:
|
| Product Name: | Black Silicon Carbide 98.57% | F. C.: | 0.20% |
|---|---|---|---|
| Fe2O3: | 0.16% | Application: | Abrasives Wheels |
| Size: | Customer's Requirement | Bulk Density: | 1.45-1.56g/cm3 |
| High Light: | 36# Black Silicon Carbide,30# Black Silicon Carbide,Carborundum Grit |
||
24# 30# 36# Black Silicon Carbide SiC 98.5% for Abrasives Cutting Wheels and Grinding Wheels
1. Black Silicon Carbide Introduction
Pure silicon carbide can be made by the so-called Lely process, in which SiC powder is sublimated into high-temperature species of silicon, carbon, silicon dicarbide (SiC2), and disilicon carbide (Si2C) in an argon gas ambient at 2500 °C and redeposited into flake-like single crystals,sized up to 2×2 cm, at a slightly colder substrate. This process yields high-quality single crystals, mostly of 6H-SiC phase (because of high growth temperature). A modified Lely process involving induction heating in graphite crucibles yields even larger single crystals of 4 inches (10 cm) in diameter, having a section 81 times larger compared to the conventional Lely process.Cubic SiC is usually grown by the more expensive process of chemical vapor deposition (CVD).Homoepitaxial and heteroepitaxial SiC layers can be grown employing both gas and liquid phase approaches.Pure silicon carbide can also be prepared by the thermal decomposition of a polymer, poly(methylsilyne), under an inert atmosphere at low temperatures. Relative to the CVD process, the pyrolysis method is advantageous because the polymer can be formed into various shapes prior to thermalization into the ceramic.
2. Black Silicon Carbide Chemical Composition (%)
| Grit | Sic | F.C. | Fe2O3 |
| F12-F90 | ≥98.50 | <0.20 | ≤0.60 |
| F100-F150 | ≥98.00 | <0.30 | ≤0.80 |
| F180-F220 | ≥97.00 | <0.30 | ≤1.20 |
| F230-F400 | ≥96.00 | <0.40 | ≤1.20 |
| F500-F800 | ≥95.00 | <0.40 | ≤1.20 |
| F1000-F1200 | ≥93.00 | <0.50 | ≤1.20 |
| P12-P90 | ≥98.50 | <0.20 | ≤0.60 |
| P100-P150 | ≥98.00 | <0.30 | ≤0.80 |
| P180-P220 | ≥97.00 | <0.30 | ≤1.20 |
| P230-P500 | ≥96.00 | <0.40 | ≤1.20 |
| P600-P1500 | ≥95.00 | <0.40 | ≤1.20 |
| P2000-P2500 | ≥93.00 | <0.50 | ≤1.20 |
3. Black Silicon Carbide Physical Index
| Grits | Bulk Density g/cm3 |
High Density g/cm3 |
Grits | Bulk Density g/cm3 |
High Density g/cm3 |
| F16 ~ F24 | 1.42~1.50 | ≥1.50 | F100 | 1.36~1.45 | ≥1.45 |
| F30 ~ F40 | 1.42~1.50 | ≥1.50 | F120 | 1.34~1.43 | ≥1.43 |
| F46 ~ F54 | 1.43~1.51 | ≥1.51 | F150 | 1.32~1.41 | ≥1.41 |
| F60 ~ F70 | 1.40~1.48 | ≥1.48 | F180 | 1.31~1.40 | ≥1.40 |
| F80 | 1.38~1.46 | ≥1.46 | F220 | 1.31~1.40 | ≥1.40 |
| F90 | 1.38~1.45 | ≥1.45 |
4. Black Silicon Carbide Size Available
F12-F1200, P12-P2500
0-1mm, 1-3mm, 6/10, 10/18, 200mesh, 325mesh
Other special specifications could be supplied on request.
5. Black Silicon Carbide Applications
F12-F14,use for sandblasting,rust removal,snagging,heavy duty grinding of steel ingot,leather,salt,floor boards.
F14-F30,use for casting play burr,cutting billet and steel tube,flat kibbling,steel ingot grinding,marble grinding,or as refractory material.
F30-F60,use for surface abrasion,outside&surface grinding,centerless grinding,tool grinding of quenching or no-quenching steel profiles,copper or other hard metal.
F60-F100,use for precision grinding, cutter sharpening,gear grinding,etc.
F100-F240,use for cutter sharpening,rough grinding,precision grinding,thread grinding.
F280-F600,use for precision grinding&thread grinding of instrument and matter an gear products.
F600-F2000,super-precision polishing,mirror polishing,surface lapping,etc.
6. Black Silicon Carbide acking
1. 25kg woven bag, 40 woven bags/jumbo bag.
2. 25kg woven bag, 40 woven bags/pallet
3. 25kg paper bag, 40 paper bags/pallet
4. 25kg paper bag, 40 paper bags/paper box
Contact Person: Jason Chen
Tel: 86-18603794999